PVC Celuka Sheet is a combination of PVC resin and inorganic that formed in molding with adopting series advanced technology, whom we normally can see his finally different shapes to be shown as wood/plastic sheets, section & bars.
There is no glue adhesion used during production, no harmful substances like formaldehyde, benzene, ammonia and trichloroethylene. It shows excellent ability in UVR, dyeing force, heat insulation, soundproof, acid and alkali-resistant, insulation, fire resistance, rot proof, moth and damp proof. Sawing, planing and nailing such kind of machining performances also been played really well by this 100% recycled sheets. Nowadays, it is a new material to replace traditional woods. With comparing to PVC Free Form Sheets, PVC Celuka Sheets talking unique advantages at points of hardness, smoothness, flatness, strength and nailwithdraw as well.
PVC celuka sheet/board is becoming the substitution of wood in many fields such as AD and Decoration. It made through foaming and pressing into shape with additives. The main material is PVC. So it covers not only features of woodplast, but also very light and can be printed, engraved easily.
Application:
1. Exhibition desk, Shelve in supermarket
2. Advertisemen Board and sign board
3. The advertisement sheet for printing, engraving, cutting, sawing
3. Architectural decoration and upholstery
4. Decoration for partition wall and shopwindows
Good features:
Features:
1, light weight, good tenacity, high rigidity
2, fireproof and flame regardant
3, good insulation
4, no sopping, no deformation
5, easily to processed
6, good plasticity, being an excellent thermoform material
7, sub-light surface and elegant vision
8, anti-chemical corrosion
9, suitable to silk screen printing
10, with imported dyes, unfading and anti-aging
Specification:
Width: 1.22m, 1.56m, 2.05m etc.
Length: 2.44m, 3.05m (as your requirement)
Thickness: 5mm~25mm
Density: 0.5-0.9
Colors: White, black, yellow, blue, green, red, all kinds of colors as requirement.
| Project |
Index |
| tensive - strength ( MPa ) |
>=12 |
| Shao hardness D |
>=55 |
| charpy notched impact strength ( kj/m2 ) |
>=14 |
| elongation at break (%) |
>=12 |
| heating size change ratio (%) |
>=12 |
| vicat softening point (%) |
+/- 2.0 |
| softening point (ºC) |
>=73 |
| flexural strength ( MPa) |
>=22 |
| flexile modulus ( MPa ) |
>=650 |
| strength of holding screw (N) |
>=750 |
| water absorption (%) |
<=1.0 |
| surface density ( kg/m3 ) |
<=750 |